分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: The realization of ultrahigh quality (Q) resonators regardless of the underpinning material platforms has been a ceaseless pursuit, because the high Q resonators provide an extreme environment of storage of light to enable observations of many unconventional nonlinear optical phenomenon with high efficiencies. Here, we demonstrate an ultra-high Q factor (7.1*10^6) microresonator on the 4H-silicon-carbide-on-insulator (4H-SiCOI) platform in which both \c{hi}^(2) and \c{hi}^(3) nonlinear processes of high efficiencies have been generated. Broadband frequency conversions, including second-, third-, fourth-harmonic generation were observed. Cascaded Raman lasing was demonstrated in the SiC microresonator for the first time to the best of our knowledge. Broadband Kerr frequency combs covering from 1300 to 1700 nm were achieved using a dispersion-engineered SiC microresonator. Our demonstration is a significant milestone in the development of SiC photonic integrated devices.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate an electrically driven compact hybrid lithium niobate microring laser by butt coupling a commercial 980-nm pump laser diode chip with a high quality Er3+-doped lithium niobate microring chip. Single mode lasing emission at 1531 nm wavelength from the Er3+-doped lithium niobate microring can be observed with the integrated 980-nm laser pumping. The compact hybrid lithium niobate microring laser occupies the chip size of 3 mmx4mmx0.5 mm. The threshold pumping laser power is 6 mW and the threshold current is 0.5 A (operating voltage 1.64 V) in the atmospheric temperature. The spectrum featuring single mode lasing with small linewidth of 0.05 nm is observed. This work explores a robust hybrid lithium niobate microring laser source which has potential applications in coherent optical communication and precision metrology.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: Integrated thin-film lithium niobate (LN) electro-optic (EO) modulators of broad bandwidth, low insertion loss, low cost and high production rate are essential elements in contemporary inter-connection industries and disruptive applications. Here, we demonstrated the design and fabri-cation of a high performance thin-film LN EO modulator using photolithography assisted chemo-mechanical etching (PLACE) technology. Our device shows a 3-dB bandwidth over 50 GHz, along with a comparable low half wave voltage-length product of 2.16 Vcm. We obtain a fiber-to-fiber insertion loss of 2.6 dB.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We report the fabrication and optical characterization of Yb3+-doped waveguide amplifiers (YDWA) on the thin film lithium niobate fabricated by photolithography assisted chemo-mechanical etching. The fabricated Yb3+-doped lithium niobate waveguides demonstrates low propagation loss of 0.13 dB/cm at 1030 nm and 0.1 dB/cm at 1060 nm. The internal net gain of 5 dB at 1030 nm and 8 dB at 1060 nm are measured on a 4.0 cm long waveguide pumped by 976nm laser diodes, indicating the gain per unit length of 1.25 dB/cm at 1030 nm and 2 dB/cm at 1060 nm, respectively. The integrated Yb3+-doped lithium niobate waveguide amplifiers will benefit the development of a powerful gain platform and are expected to contribute to the high-density integration of thin film lithium niobate based photonic chip.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate monolithic integration of an electro-optically (EO) tunable microring laser on lithium niobate on insulator (LNOI) platform. The device is fabricated by photolithography assisted chemo-mechanical etching (PLACE), and the pump laser is evanescently coupled into the erbium (Er3+) doped LN microring laser using an undoped LN waveguide mounted above the microring. The quality factor of the LN microring resonator is measured as high as 1.54x10^5 at the wavelength of 1542 nm. Lasing action can be observed at a pump power threshold below 3.5 mW using a 980 nm continuous-wave pump laser. Finally, tuning of the laser wavelength is achieved by varying the electric voltage on the microelectrodes fabricated in the vicinity of microring waveguide, showing an EO coefficient of 0.33 pm/V.