分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: Quantum coherence in quantum optics is an essential part of optical information processing and light manipulation. Alkali metal vapors, despite the numerous shortcomings, are traditionally used in quantum optics as a working medium due to convenient near-infrared excitation, strong dipole transitions and long-lived coherence. Here, we proposed and experimentally demonstrated photon retention and subsequent re-emittance with the quantum coherence in a system of coherently excited molecular nitrogen ions (N2+) which are produced using a strong 800 nm femtosecond laser pulse. Such photon retention, facilitated by quantum coherence, keeps releasing directly-unmeasurable coherent photons for tens of picoseconds, but is able to be read-out by a time-delayed femtosecond pulse centered at 1580 nm via two-photon resonant absorption, resulting in a strong radiation at 329.3 nm. We reveal a pivotal role of the excited-state population to transmit such extremely weak re-emitted photons in this system. This new finding unveils the nature of the coherent quantum control in N2+ for the potential platform for optical information storage in the remote atmosphere, and facilitates further exploration of fundamental interactions in the quantum optical platform with strong-field ionized molecules.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We report the fabrication and optical characterization of Yb3+-doped waveguide amplifiers (YDWA) on the thin film lithium niobate fabricated by photolithography assisted chemo-mechanical etching. The fabricated Yb3+-doped lithium niobate waveguides demonstrates low propagation loss of 0.13 dB/cm at 1030 nm and 0.1 dB/cm at 1060 nm. The internal net gain of 5 dB at 1030 nm and 8 dB at 1060 nm are measured on a 4.0 cm long waveguide pumped by 976nm laser diodes, indicating the gain per unit length of 1.25 dB/cm at 1030 nm and 2 dB/cm at 1060 nm, respectively. The integrated Yb3+-doped lithium niobate waveguide amplifiers will benefit the development of a powerful gain platform and are expected to contribute to the high-density integration of thin film lithium niobate based photonic chip.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate an on-chip Yb3+-doped lithium niobate (LN) microdisk laser. The intrinsic quality factors of the fabricated Yb3+-doped LN microdisk resonator are measured up to 3.79x10^5 at 976 nm wavelength and 1.1x10^6 at 1514 nm wavelength. The multi-mode laser emissions are obtained in a band from 1020 nm to 1070 nm pumped by 984 nm laser and with the low threshold of 103 {\mu}W, resulting in a slope efficiency of 0.53% at room temperature. Furthermore, the second-harmonic frequency of pump light and the sum-frequency of the pump light and laser emissions are both generated in the on-chip Yb3+-doped LN microdisk benefited from the strong \c{hi}(2) nonlinearity of LN. These microdisk lasers are expected to contribute to the high-density integration of LNOI-based photonic chip.