分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate a non-invasive time-sorting method for ultrafast electron diffraction (UED) experiments with radio-frequency (rf) compressed electron beams. We show that electron beam energy and arrival time at the sample after rf compression are strongly correlated such that the arrival time jitter may be corrected through measurement of the beam energy. The method requires minimal change to the infrastructure of most of the UED machines and is applicable to both keV and MeV UED. In our experiment with ~3 MeV beam, the timing jitter after rf compression is corrected with 35 fs root-mean-square (rms) accuracy, limited by the 3x10^-4 energy stability. For keV UED with high energy stability, sub-10 fs accuracy in time-sorting should be readily achievable. This time-sorting technique allows us to retrieve the 2.5 THz oscillation related to coherent A1g phonon in laser excited Bismuth film and extends the temporal resolution of UED to a regime far beyond the 100-200 fs rms jitter limitation.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate an on-chip single-mode Er3+-doped thin film lithium niobate (Er: TFLN) laser which consists of a Fabry-P\'erot (FP) resonator based on Sagnac loop reflectors (SLRs). The fabricated Er: TFLN laser has a footprint of 6.5 mmx1.5 mm with a loaded quality (Q) factor of 1.6x105 and a free spectral range (FSR) of 63 pm. We generate the single-mode laser around 1550-nm wavelength with a maximum output power of 44.7 {\mu}W and a slope efficiency of 0.18 %.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate monolithic integration of an electro-optically (EO) tunable microring laser on lithium niobate on insulator (LNOI) platform. The device is fabricated by photolithography assisted chemo-mechanical etching (PLACE), and the pump laser is evanescently coupled into the erbium (Er3+) doped LN microring laser using an undoped LN waveguide mounted above the microring. The quality factor of the LN microring resonator is measured as high as 1.54x10^5 at the wavelength of 1542 nm. Lasing action can be observed at a pump power threshold below 3.5 mW using a 980 nm continuous-wave pump laser. Finally, tuning of the laser wavelength is achieved by varying the electric voltage on the microelectrodes fabricated in the vicinity of microring waveguide, showing an EO coefficient of 0.33 pm/V.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We report the fabrication and optical characterization of Yb3+-doped waveguide amplifiers (YDWA) on the thin film lithium niobate fabricated by photolithography assisted chemo-mechanical etching. The fabricated Yb3+-doped lithium niobate waveguides demonstrates low propagation loss of 0.13 dB/cm at 1030 nm and 0.1 dB/cm at 1060 nm. The internal net gain of 5 dB at 1030 nm and 8 dB at 1060 nm are measured on a 4.0 cm long waveguide pumped by 976nm laser diodes, indicating the gain per unit length of 1.25 dB/cm at 1030 nm and 2 dB/cm at 1060 nm, respectively. The integrated Yb3+-doped lithium niobate waveguide amplifiers will benefit the development of a powerful gain platform and are expected to contribute to the high-density integration of thin film lithium niobate based photonic chip.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate an on-chip Yb3+-doped lithium niobate (LN) microdisk laser. The intrinsic quality factors of the fabricated Yb3+-doped LN microdisk resonator are measured up to 3.79x10^5 at 976 nm wavelength and 1.1x10^6 at 1514 nm wavelength. The multi-mode laser emissions are obtained in a band from 1020 nm to 1070 nm pumped by 984 nm laser and with the low threshold of 103 {\mu}W, resulting in a slope efficiency of 0.53% at room temperature. Furthermore, the second-harmonic frequency of pump light and the sum-frequency of the pump light and laser emissions are both generated in the on-chip Yb3+-doped LN microdisk benefited from the strong \c{hi}(2) nonlinearity of LN. These microdisk lasers are expected to contribute to the high-density integration of LNOI-based photonic chip.