分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: The realization of ultrahigh quality (Q) resonators regardless of the underpinning material platforms has been a ceaseless pursuit, because the high Q resonators provide an extreme environment of storage of light to enable observations of many unconventional nonlinear optical phenomenon with high efficiencies. Here, we demonstrate an ultra-high Q factor (7.1*10^6) microresonator on the 4H-silicon-carbide-on-insulator (4H-SiCOI) platform in which both \c{hi}^(2) and \c{hi}^(3) nonlinear processes of high efficiencies have been generated. Broadband frequency conversions, including second-, third-, fourth-harmonic generation were observed. Cascaded Raman lasing was demonstrated in the SiC microresonator for the first time to the best of our knowledge. Broadband Kerr frequency combs covering from 1300 to 1700 nm were achieved using a dispersion-engineered SiC microresonator. Our demonstration is a significant milestone in the development of SiC photonic integrated devices.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We report the fabrication and optical characterization of Yb3+-doped waveguide amplifiers (YDWA) on the thin film lithium niobate fabricated by photolithography assisted chemo-mechanical etching. The fabricated Yb3+-doped lithium niobate waveguides demonstrates low propagation loss of 0.13 dB/cm at 1030 nm and 0.1 dB/cm at 1060 nm. The internal net gain of 5 dB at 1030 nm and 8 dB at 1060 nm are measured on a 4.0 cm long waveguide pumped by 976nm laser diodes, indicating the gain per unit length of 1.25 dB/cm at 1030 nm and 2 dB/cm at 1060 nm, respectively. The integrated Yb3+-doped lithium niobate waveguide amplifiers will benefit the development of a powerful gain platform and are expected to contribute to the high-density integration of thin film lithium niobate based photonic chip.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate an on-chip Yb3+-doped lithium niobate (LN) microdisk laser. The intrinsic quality factors of the fabricated Yb3+-doped LN microdisk resonator are measured up to 3.79x10^5 at 976 nm wavelength and 1.1x10^6 at 1514 nm wavelength. The multi-mode laser emissions are obtained in a band from 1020 nm to 1070 nm pumped by 984 nm laser and with the low threshold of 103 {\mu}W, resulting in a slope efficiency of 0.53% at room temperature. Furthermore, the second-harmonic frequency of pump light and the sum-frequency of the pump light and laser emissions are both generated in the on-chip Yb3+-doped LN microdisk benefited from the strong \c{hi}(2) nonlinearity of LN. These microdisk lasers are expected to contribute to the high-density integration of LNOI-based photonic chip.