分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate a robust low-loss optical interface by tiling passive (i.e., without doping of active ions) thin film lithium niobate (TFLN) and active (i.e., doped with rare earth ions) TFLN substrates for monolithic integration of passive/active lithium niobate photonics. The tiled substrates composed of both active and passive areas allow to pattern the mask of the integrated active passive photonic device at once using a single continuous photolithography process. The interface loss of tiled substrate is measured as low as 0.26 dB. Thanks to the stability provided by this approach, a four-channel waveguide amplifier is realized in a straightforward manner, which shows a net gain of ~5 dB at 1550-nm wavelength and that of ~8 dB at 1530-nm wavelength for each channel. The robust low-loss optical interface for passive/active photonic integration will facilitate large-scale high performance photonic devices which require on-chip light sources and amplifiers.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We overcome the difficulty in realizing a monolithic waveguide-coupled microring laser integrated on erbium-doped thin film lithium niobate (Er: TFLN) using photolithography assisted chemo-mechanical etching (PLACE) technique. We demonstrate an integrated single-frequency microring laser operating around 1531 nm wavelength. The PLACE technique, enabling integrated Er: TFLN photonics with low propagation loss, can thus be used to realize low cost mass production of monolithic on-chip microlasers with applications ranging from optical communication and photonic integrated circuit (PIC) to precision metrology and large-scale sensing.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We demonstrate an electrically driven compact hybrid lithium niobate microring laser by butt coupling a commercial 980-nm pump laser diode chip with a high quality Er3+-doped lithium niobate microring chip. Single mode lasing emission at 1531 nm wavelength from the Er3+-doped lithium niobate microring can be observed with the integrated 980-nm laser pumping. The compact hybrid lithium niobate microring laser occupies the chip size of 3 mmx4mmx0.5 mm. The threshold pumping laser power is 6 mW and the threshold current is 0.5 A (operating voltage 1.64 V) in the atmospheric temperature. The spectrum featuring single mode lasing with small linewidth of 0.05 nm is observed. This work explores a robust hybrid lithium niobate microring laser source which has potential applications in coherent optical communication and precision metrology.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: Integrated thin-film lithium niobate (LN) electro-optic (EO) modulators of broad bandwidth, low insertion loss, low cost and high production rate are essential elements in contemporary inter-connection industries and disruptive applications. Here, we demonstrated the design and fabri-cation of a high performance thin-film LN EO modulator using photolithography assisted chemo-mechanical etching (PLACE) technology. Our device shows a 3-dB bandwidth over 50 GHz, along with a comparable low half wave voltage-length product of 2.16 Vcm. We obtain a fiber-to-fiber insertion loss of 2.6 dB.
分类: 光学 >> 量子光学 提交时间: 2023-02-19
摘要: We report the fabrication and optical characterization of Yb3+-doped waveguide amplifiers (YDWA) on the thin film lithium niobate fabricated by photolithography assisted chemo-mechanical etching. The fabricated Yb3+-doped lithium niobate waveguides demonstrates low propagation loss of 0.13 dB/cm at 1030 nm and 0.1 dB/cm at 1060 nm. The internal net gain of 5 dB at 1030 nm and 8 dB at 1060 nm are measured on a 4.0 cm long waveguide pumped by 976nm laser diodes, indicating the gain per unit length of 1.25 dB/cm at 1030 nm and 2 dB/cm at 1060 nm, respectively. The integrated Yb3+-doped lithium niobate waveguide amplifiers will benefit the development of a powerful gain platform and are expected to contribute to the high-density integration of thin film lithium niobate based photonic chip.